Metal Casting: Advantages of Metal Casting, Limitations of Metal Casting, History of Metal Casting, Metal Casting History (India), Terms used in Metal Casting, Flask, Pattern, Parting line, Molding sand, Facing sand, Core, Pouring basin, Sprue, Runner, Gate, Chaplets, Riser

Metal Casting

Introduction

Virtually nothing moves, turns, rolls, or flies without the benefit of cast metal products. The metal casting industry plays a key role in all the major sectors of our economy. There are castings in locomotives, cars trucks, aircraft, office buildings, factories, schools, and homes. Figure some metal cast parts.

Metal Casting is one of the oldest materials shaping methods known. Casting means pouring molten metal into a mold with a cavity of the shape to be made, and allowing it to solidify. When solidified, the desired metal object is taken out from the mold either by breaking the mold or taking the mold apart. The solidified object is called the casting. By this process, intricate parts can be given strength and rigidity frequently not obtainable by any other manufacturing process. The mold, into which the metal is poured, is made of some heat resisting material. Sand is most often used as it resists the high temperature of the molten metal. Permanent molds of metal can also be used to cast products.

Metal Casting: Advantages of Metal Casting, Limitations of Metal Casting, History of Metal Casting, Metal Casting History (India), Terms used in Metal Casting,  Flask, Pattern,  Parting line, Molding sand, Facing sand, Core, Pouring basin, Sprue, Runner, Gate, Chaplets, Riser
Metal Casting



Advantages ofย Metal Casting

The metal casting process is extensively used in manufacturing because of its many advantages.

1. Molten material can flow into very small sections so that intricate shapes can be made by this process. As a result, many other operations, such as machining, forging, and welding, can be minimized or eliminated.

2. It is possible to cast practically any material that is ferrous or non-ferrous.

3. As the metal can be placed exactly where it is required, large saving in weight can be achieved.

4. The necessary tools required for casting molds are very simple and inexpensive. As a result, for production of a small lot, it is the ideal process.

5. There are certain parts made from metals and alloys that can only be processed this way.

6. Size and weight of the product is not a limitation for the casting process.

Limitations ofย Metal Casting

1. Dimensional accuracy and surface finish of the castings made by sand casting processes are a limitation to this technique. Many new casting processes have been developed which can take into consideration the aspects of dimensional accuracy and surface finish. Some of these processes are die casting process, investment casting process, vacuum-sealed molding process, and shell molding process.

2. The metal casting process is a labor intensive process

History ofย Metal Casting

Casting technology, according to biblical records, reaches back almost 5,000 years BC. Gold, pure in nature, most likely caught Prehistoric manโ€™s fancyโ€ฆas he probably hammered gold ornaments out of the gold nuggets he found. Silver would have been treated similarly. Mankind next found copper, because it appeared in the ash of his camp fires from copper-bearing ore that he lined his fire pits with. Man soon found that copper was harder than gold or silver. Copper did not bend up when used. So copper, found a โ€˜nitchโ€™ in manโ€™s early tools, and then marched itโ€™s way into Weaponry. But, long before all thisโ€ฆman found clay. So he made pottery โ€“ something to eat from. Then he thought, โ€œnowโ€ฆwhat else can I do with this mudโ€ฆโ€ . Early man thought about it, โ€œthey used this pottery stuff, ( the first patterns ), to shape metal into bowls โ€œ.

3200 B.C. A copper frog, the oldest known casting in existence, is cast in Mesopotamia. 233 B.C. Cast iron plowshares are poured in China.

500 A.D. Cast crucible steel is first produced in India, but the process is lost until 1750, when Benjamin Huntsman reinvents it in England.

1455 Dillenburg Castle in Germany is the first to use cast iron pipe to transport water. 1480 Birth of Vannoccio Biringuccio (1480-1539), the โ€œfather of the foundry industry,โ€ in Italy. He is the first man to document the foundry process in writing.

1709 Englishman Abraham Darby creates the first true foundry flask for sand and loam molding.

1750 Benjamin Huntsman reinvents the process of cast crucible steel in England. This process is the first in which the steel is completely melted, producing a uniform composition within the melt. Since the metal is completely molten, it also allows for alloy steel production, as the additional elements in the alloy can be added to the crucible during melting. Prior steel production was accomplished by a combination of forging and tempering, and the metal never reached a molten state.

1809 Centrifugal casting is developed by A. G. Eckhardt of Soho, England.

1896 American Foundrymenโ€™s Association (renamed American Foundrymenโ€™s Society in 1948 and now called the American Foundry Society) is formed.

1897 Investment casting is rediscovered by B.F. Philbrook of Iowa. He uses it to cast dental inlays.

1947 The Shell process, invented by J. Croning of Germany during WWII, is discovered by U.S. officials and made public.

1953 The Hotbox system of making and curing cores in one operation is developed, eliminating the need for dielectric drying ovens.

1958 H.F. Shroyer is granted a patent for the full mold process, the forerunner of the expendable pattern (lost foam) casting process.

1968 The Coldbox process is introduced by L. Toriello and J. Robins for high production core making.

1971 The Japanese develop V-Process molding. This method uses unbonded sand and a vacuum. 1971 Rheocasting is developed at Massachusetts Institute of Technology. 1996 Cast metal matrix composites are first used in a production model automobile in the brake rotors for the Lotus Elise.

Metal Casting History (India)

3000 BC Earliest castings include the 11 cm high bronze dancing girl found at Mohen-jo-daro.

2000 BC Iron pillars, arrows, hooks, nails, bowls and daggers or earlier have been found in Delhi, Roopar, Nashik and other places.

500 BC Large scale state-owned mints and jewelry units, and processes of metal extraction and alloying have been mentioned in Kautilyaโ€™s Arthashastra

500 A.D. Cast crucible steel is first produced in India, but the process is lost until 1750, when Benjamin Huntsman reinvents it in England.

Terms used inย Metal Casting

1. Flask:ย 

A metal or wood frame, without fixed top or bottom, in which the mold is formed. Depending upon the position of the flask in the molding structure, it is referred to by various names such as drag โ€“ lower molding flask, cope โ€“ upper molding flask, cheek โ€“ intermediate molding flask used in three piece molding.

2. Pattern:ย 

It is the replica of the final object to be made. The mold cavity is made with the help of pattern.

3. Parting line:ย 

This is the dividing line between the two molding flasks that makes up the mold.

4. Molding sand:ย 

Sand, which binds strongly without losing its permeability to air or gases. It is a mixture of silica sand, clay, and moisture in appropriate proportions.

5. Facing sand:ย 

The small amount of carbonaceous material sprinkled on the inner surface of the mold cavity to give a better surface finish to the castings.

6. Core:ย 

A separate part of the mold, made of sand and generally baked, which is used to create openings and various shaped cavities in the castings.

7. Pouring basin:ย 

A small funnel shaped cavity at the top of the mold into which the molten metal is poured.

8. Sprue:ย 

The passage through which the molten metal, from the pouring basin, reaches the mold cavity. In many cases it controls the flow of metal into the mold.

9. Runner:ย 

The channel through which the molten metal is carried from the sprue to the gate.

10. Gate:ย 

A channel through which the molten metal enters the mold cavity.

11. Chaplets:ย 

Chaplets are used to support the cores inside the mold cavity to take care of its own weight and overcome the metallostatic force.

12. Riser:ย 

A column of molten metal placed in the mold to feed the castings as it shrinks and solidifies. Also known as โ€œfeed headโ€.

13. Vent:ย 

Small opening in the mold to facilitate escape of air and gases.